PLA-CF

High-Strength PLA Carbon Fiber Filament

High-Strength PLA Carbon Fiber Filament, rigidity, dimensional stability, and a professional matte finish.

Consistent Quality

Smooth Printing

High  Strength

Carbon    Fiber

High    Rigidity

Reinforced with 15% Carbon Fiber Filament

A 15% carbon-fiber formulation gives PLA-CF greater rigidity and a refined technical finish for functional prototypes and engineering-focused applications.

Engineered for Demanding Parts

Enhanced mechanical performance makes PLA-CF well suited for fixtures, brackets, housings, tooling, and prototypes that require a more rigid material response.

High-Strength PLA Carbon Fiber Filament for Rigid Parts

Combining mechanical strength, rigidity, chemical resistance, and corrosion resistance, PLA-CF supports durable components for demanding operational environments.

Your browser does not support HTML5 video.

PARAMETER INFORMATION

PLA-CF

Functional FDM Filament

PRINT SETTINGS
Pre-Print Drying (Filament Dryer)	50±5°C, 4-8h	Print & Storage Humidity	<20% RH (Sealed with desiccant)
Nozzle Temperature	210°C-240°C	Nozzle Diameter	0.4/0.6/0.8mm
Build Plate Type	Cool Plate SuperTack/Textured PEI Plate/Smooth PEI Plate	Build Plate Temperature	55-65°C
Cooling Fan	100%	Print Speed	50-200mm/s
Retraction Distance	0.6-1.0mm	Retraction Speed	20-40mm/s
Chamber Temperature	25-45°C	Max. Overhang Angle	55°
Max. Bridge Length	30mm	Build Plate Surface Treatment	No treatment required

MECHANICAL PROPERTIES

Tensile Strength / MPa	Elongation at Break / %	Flexural Modulus / MPa	Flexural Strength / MPa	Impact Strength / kJ/m2
38	8	3950	89	23

Recommended values may be fine-tuned for printer model, geometry, and ambient conditions.